Effect of PEGDE addition on rheological and mechanical properties of bisphenol E cyanate ester

TitleEffect of PEGDE addition on rheological and mechanical properties of bisphenol E cyanate ester
Publication TypeJournal Article
Year of Publication2013
AuthorsSheng X, Hanus R, Bauer A, Kessler MR
Journal TitleJournal of Applied Polymer Science
Volume130
Pages463-469
Date Published10
Type of ArticleArticle
ISBN Number0021-8995
Accession NumberWOS:000321305500055
Keywordsblends, cyanic acid, epoxy-resin matrices, glass transition, glycidylethers, layered silicate nanocomposites, mechanical properties, moisture absorption, polyfunctional, POLYMERS, processability, resins, thermosets
Abstract

Cyanate esters are a group of resins with exceptional thermal and mechanical properties and are often blended with lower cost epoxy resins. These blends are often brittle, and a toughening method, such as the addition of soft segments, is necessary. Poly(ethylene glycol) diglycidyl ether, or PEGDE, was added to bisphenol E cyanate ester as a toughening agent. PEGDE was added at loadings of 0-30 wt %, and rheological and mechanical properties were analyzed after curing. As PEGDE loading was increased, the gel point increased accordingly while the activation energy of gelation decreased, indicating PEGDE accelerated the gelation process. Dynamic mechanical analysis results indicated a decrease in glass transition temperature as the PEGDE loading increased. Three-point bending tests yielded similar toughness to the neat BECy at low PEGDE loadings, with a dramatic increase at loadings of 25 and 30 wt % PEGDE. (c) 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013